- •Isbn: 3-527-30999-3
- •Introduction
- •Isbn: 3-527-30999-3
- •1072 1 Introduction
- •Isbn: 3-527-30999-3
- •Inventor of stone groundwood. Right: the second version
- •1074 2 A Short History of Mechanical Pulping
- •In refining, the thinnings (diameter 7–10cm) can also be processed.
- •In mechanical pulping as it causes foam; the situation is especially
- •In mechanical pulping, those fibers that are responsible for strength properties
- •Isbn: 3-527-30999-3
- •In mechanical pulping, the wood should have a high moisture content, and the
- •In the paper and reduced paper quality. The higher the quality of the paper, the
- •1076 3 Raw Materials for Mechanical Pulp
- •1, Transversal resistance; 2, Longitudinal resistance; 3, Tanning limit.
- •3.2 Processing of Wood 1077
- •In the industrial situation in order to avoid problems of pollution and also
- •1078 3 Raw Materials for Mechanical Pulp
- •2, Grinder pit; 3, weir; 4, shower water pipe;
- •5, Wood magazine; 6, finger plate; 7, pulp stone
- •Isbn: 3-527-30999-3
- •4.1.2.1 Softening of the Fibers
- •1080 4 Mechanical Pulping Processes
- •235 °C, whereas according to Styan and Bramshall [4] the softening temperatures
- •Isolated lignin, the softening takes place at 80–90 °c, and additional water
- •4.1 Grinding Processes 1081
- •1082 4 Mechanical Pulping Processes
- •1, Cool wood; 2, strongly heated wood layer; 3, actual grinding
- •4.1.2.2 Defibration (Deliberation) of Single Fibers from the Fiber Compound
- •4 Mechanical Pulping Processes
- •Influence of Parameters on the Properties of Groundwood
- •In the mechanical defibration of wood by grinding, several process parameters
- •Improved by increasing both parameters – grinding pressure and pulp stone
- •In practice, the temperature of the pit pulp is used to control the grinding process,
- •In Fig. 4.8, while the grit material of the pulp stone estimates the microstructure
- •4 Mechanical Pulping Processes
- •4.1 Grinding Processes
- •Is of major importance for process control in grinding.
- •4 Mechanical Pulping Processes
- •4.1.4.2 Chain Grinders
- •Is fed continuously, as shown in Fig. 4.17.
- •Initial thickness of the
- •4 Mechanical Pulping Processes
- •Include:
- •Increases; from the vapor–pressure relationship, the boiling temperature is seen
- •4 Mechanical Pulping Processes
- •In the pgw proves, and to prevent the colder seal waters from bleeding onto the
- •4.1 Grinding Processes
- •In pressure grinding, the grinder shower water temperature and flow are
- •70 °C, a hot loop is no longer used, and the grinding process is
- •4 Mechanical Pulping Processes
- •Very briefly at a high temperature and then refined at high
- •4.2 Refiner Processes
- •4 Mechanical Pulping Processes
- •Intensity caused by plate design and rotational speed.
- •4.2 Refiner Processes
- •1. Reduction of the chips sizes to units of matches.
- •2. Reduction of those “matches” to fibers.
- •3. Fibrillation of the deliberated fibers and fiber bundles.
- •1970S as result of the improved tmp technology. Because the key subprocess in
- •4 Mechanical Pulping Processes
- •Impregnation Preheating Cooking Yield
- •30%. Because of their anatomic structure, hardwoods are able to absorb more
- •Is at least 2 mWh t–1 o.D. Pulp for strongly fibrillated tmp and ctmp pulps from
- •4 Mechanical Pulping Processes
- •4.2 Refiner Processes
- •1500 R.P.M. (50 Hz) or 1800 r.P.M. (60 Hz); designed pressure 1.4 mPa
- •1500 R.P.M. (50 Hz) or 1800 r.P.M. (60 Hz); designed pressure 1.4 mPa;
- •4.2 Refiner Processes
- •4 Mechanical Pulping Processes
- •In hardwoods makes them more favorable than softwoods for this purpose. A
- •4.2 Refiner Processes
- •Isbn: 3-527-30999-3
- •1114 5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5.2Machines and Aggregates for Screening and Cleaning 1115
- •In refiner mechanical pulping, there is virtually no such coarse material in the
- •1116 5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5.2Machines and Aggregates for Screening and Cleaning
- •5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5.3 Reject Treatment and Heat Recovery
- •55% Iso and 65% iso. The intensity of the bark removal, the wood species,
- •Isbn: 3-527-30999-3
- •1124 6 Bleaching of Mechanical Pulp
- •Initially, the zinc hydroxide is filtered off and reprocessed to zinc dust. Then,
- •2000 Kg of technical-grade product is common. Typically, a small amount of a chelant
- •6.1 Bleaching with Dithionite 1125
- •Vary, but are normally ca. 10 kg t–1 or 1% on fiber. As the number of available
- •1126 6 Bleaching of Mechanical Pulp
- •6.2 Bleaching with Hydrogen Peroxide
- •70 °C, 2 h, amount of NaOh adjusted.
- •6.2 Bleaching with Hydrogen Peroxide
- •Is shown in Fig. 6.5, where silicate addition leads to a higher brightness and a
- •Volume (bulk). For most paper-grade applications, fiber volume should be low in
- •Valid and stiff fibers with a high volume are an advantage; however, this requires
- •1130 6 Bleaching of Mechanical Pulp
- •6.2 Bleaching with Hydrogen Peroxide
- •Very high brightness can be achieved with two-stage peroxide bleaching, although
- •In a first step. This excess must be activated with an addition of caustic soda. The
- •Volume of liquid to be recycled depends on the dilution and dewatering conditions
- •6 Bleaching of Mechanical Pulp
- •6 Bleaching of Mechanical Pulp
- •Is an essential requirement for bleaching effectiveness. Modern twin-wire presses
- •Is discharged to the effluent treatment plant. After the main bleaching stage, the
- •6.3 Technology of Mechanical Pulp Bleaching
- •1136 6 Bleaching of Mechanical Pulp
- •Isbn: 3-527-30999-3
- •7.3 Shows the fractional composition according to the McNett principle versus
- •1138 7 Latency and Properties of Mechanical Pulp
- •7.2 Properties of Mechanical Pulp 1139
4.1.2.2 Defibration (Deliberation) of Single Fibers from the Fiber Compound
The pressure pulsations cause deformation of the fibers in the wood. Because of
the macro structure of the pulp stone surface, the fibers will be compressed and
expanded with frequencies from 40 kHz. This leads to a breakdown of intermolecular
bondings between the fibers and of intramolecular bondings within the fiber,
as described by Atack and Pye [9]. The breakdown of bonds is the basic prerequisite
for deliberation of the fibers from the wood. In addition, these deformations
support the water absorption of lignin.
The pulp stone grit, when meeting the fiber, causes “treatment” of the fiber surface.
Depending on the macrostructure and microstructure of the pulp stone surface,
the fiber will be crushed, scratched, compressed, sheared off and cut. The
strict subsequent loosening and peeling of fibers from wood surface, starting generally
from one end of the fiber, is shown schematically in Fig. 4.5. The fiber surface
will be fibrillated, the primary wall is opened, and finally the fiber deliberated
from the fiber compound, with the “treatment"-phase lasting only 20–40 ms. The
higher the feeding speed of wood, the less a single fiber is treated until the next
grit appears.
Grit direction Grit direction
Loosening of fibers
starting from one fiber end
Subsequent peeling of
loosened fibers
Fig. 4.5 Schematic diagram of fiber loosening and peeling in
a grinding process (according to Atack [10]).
1083
4 Mechanical Pulping Processes
4.1.3
Influence of Parameters on the Properties of Groundwood
In the mechanical defibration of wood by grinding, several process parameters
have significant influences on the final properties of the stone groundwood.
Among these, the most important include:
_ Moisture of the wood logs
_ Logs feeding speed or grinding pressure respectively
_ Pulp stone rotational speed
_ Temperatures
_ Process consistency
_ Surface profile of the pulp stone
_ Specific grinding energy consumption
Basically, it can be said that an increase in grinding pressure produces a groundwood
with better dewatering behavior (high freeness) and less strength properties,
assuming that all other parameters are kept constant. Such pulps are coarse
groundwoods, whereas pulps with low freeness are fine groundwoods. Increasing
the pulp stone speed, and keeping all other conditions constant, produces a pulp
with shorter fibers and lower freeness.
From a practical standpoint, the efficiency of the grinding process will be
Improved by increasing both parameters – grinding pressure and pulp stone
speed. However, the relationship between both of these parameters can be held
constant and high-quality groundwood produced.
The temperature relationship during grinding also affects the properties of the
final groundwood. Functions which describe the temperature relationship in
grinding include:
_ Temperature of the pit pulp
_ Temperature of the shower water
_ Temperature at the end of the grinding zone