- •1072 1 Introduction
- •Isbn: 3-527-30999-3
- •Inventor of stone groundwood. Right: the second version
- •1074 2 A Short History of Mechanical Pulping
- •In refining, the thinnings (diameter 7–10cm) can also be processed.
- •In mechanical pulping as it causes foam; the situation is especially
- •In mechanical pulping, those fibers that are responsible for strength properties
- •Isbn: 3-527-30999-3
- •In mechanical pulping, the wood should have a high moisture content, and the
- •In the paper and reduced paper quality. The higher the quality of the paper, the
- •1076 3 Raw Materials for Mechanical Pulp
- •1, Transversal resistance; 2, Longitudinal resistance; 3, Tanning limit.
- •3.2 Processing of Wood 1077
- •In the industrial situation in order to avoid problems of pollution and also
- •1078 3 Raw Materials for Mechanical Pulp
- •2, Grinder pit; 3, weir; 4, shower water pipe;
- •5, Wood magazine; 6, finger plate; 7, pulp stone
- •Isbn: 3-527-30999-3
- •4.1.2.1 Softening of the Fibers
- •1080 4 Mechanical Pulping Processes
- •235 °C, whereas according to Styan and Bramshall [4] the softening temperatures
- •Isolated lignin, the softening takes place at 80–90 °c, and additional water
- •4.1 Grinding Processes 1081
- •1082 4 Mechanical Pulping Processes
- •1, Cool wood; 2, strongly heated wood layer; 3, actual grinding
- •4.1.2.2 Defibration (Deliberation) of Single Fibers from the Fiber Compound
- •4 Mechanical Pulping Processes
- •Influence of Parameters on the Properties of Groundwood
- •In the mechanical defibration of wood by grinding, several process parameters
- •Improved by increasing both parameters – grinding pressure and pulp stone
- •In practice, the temperature of the pit pulp is used to control the grinding process,
- •In Fig. 4.8, while the grit material of the pulp stone estimates the microstructure
- •4 Mechanical Pulping Processes
- •4.1 Grinding Processes
- •Is of major importance for process control in grinding.
- •4 Mechanical Pulping Processes
- •4.1.4.2 Chain Grinders
- •Is fed continuously, as shown in Fig. 4.17.
- •Initial thickness of the
- •4 Mechanical Pulping Processes
- •Include:
- •Increases; from the vapor–pressure relationship, the boiling temperature is seen
- •4 Mechanical Pulping Processes
- •In the pgw proves, and to prevent the colder seal waters from bleeding onto the
- •4.1 Grinding Processes
- •In pressure grinding, the grinder shower water temperature and flow are
- •70 °C, a hot loop is no longer used, and the grinding process is
- •4 Mechanical Pulping Processes
- •Very briefly at a high temperature and then refined at high
- •4.2 Refiner Processes
- •4 Mechanical Pulping Processes
- •Intensity caused by plate design and rotational speed.
- •4.2 Refiner Processes
- •1. Reduction of the chips sizes to units of matches.
- •2. Reduction of those “matches” to fibers.
- •3. Fibrillation of the deliberated fibers and fiber bundles.
- •1970S as result of the improved tmp technology. Because the key subprocess in
- •4 Mechanical Pulping Processes
- •Impregnation Preheating Cooking Yield
- •30%. Because of their anatomic structure, hardwoods are able to absorb more
- •Is at least 2 mWh t–1 o.D. Pulp for strongly fibrillated tmp and ctmp pulps from
- •4 Mechanical Pulping Processes
- •4.2 Refiner Processes
- •1500 R.P.M. (50 Hz) or 1800 r.P.M. (60 Hz); designed pressure 1.4 mPa
- •1500 R.P.M. (50 Hz) or 1800 r.P.M. (60 Hz); designed pressure 1.4 mPa;
- •4.2 Refiner Processes
- •4 Mechanical Pulping Processes
- •In hardwoods makes them more favorable than softwoods for this purpose. A
- •4.2 Refiner Processes
- •Isbn: 3-527-30999-3
- •1114 5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5.2Machines and Aggregates for Screening and Cleaning 1115
- •In refiner mechanical pulping, there is virtually no such coarse material in the
- •1116 5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5.2Machines and Aggregates for Screening and Cleaning
- •5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5 Processing of Mechanical Pulp and Reject Handling: Screening and Cleaning
- •5.3 Reject Treatment and Heat Recovery
- •55% Iso and 65% iso. The intensity of the bark removal, the wood species,
- •Isbn: 3-527-30999-3
- •1124 6 Bleaching of Mechanical Pulp
- •Initially, the zinc hydroxide is filtered off and reprocessed to zinc dust. Then,
- •2000 Kg of technical-grade product is common. Typically, a small amount of a chelant
- •6.1 Bleaching with Dithionite 1125
- •Vary, but are normally ca. 10 kg t–1 or 1% on fiber. As the number of available
- •1126 6 Bleaching of Mechanical Pulp
- •6.2 Bleaching with Hydrogen Peroxide
- •70 °C, 2 h, amount of NaOh adjusted.
- •6.2 Bleaching with Hydrogen Peroxide
- •Is shown in Fig. 6.5, where silicate addition leads to a higher brightness and a
- •Volume (bulk). For most paper-grade applications, fiber volume should be low in
- •Valid and stiff fibers with a high volume are an advantage; however, this requires
- •1130 6 Bleaching of Mechanical Pulp
- •6.2 Bleaching with Hydrogen Peroxide
- •Very high brightness can be achieved with two-stage peroxide bleaching, although
- •In a first step. This excess must be activated with an addition of caustic soda. The
- •Volume of liquid to be recycled depends on the dilution and dewatering conditions
- •6 Bleaching of Mechanical Pulp
- •6 Bleaching of Mechanical Pulp
- •Is an essential requirement for bleaching effectiveness. Modern twin-wire presses
- •Is discharged to the effluent treatment plant. After the main bleaching stage, the
- •6.3 Technology of Mechanical Pulp Bleaching
- •1136 6 Bleaching of Mechanical Pulp
- •Isbn: 3-527-30999-3
- •7.3 Shows the fractional composition according to the McNett principle versus
- •1138 7 Latency and Properties of Mechanical Pulp
- •7.2 Properties of Mechanical Pulp 1139
6 Bleaching of Mechanical Pulp
6.3
Technology of Mechanical Pulp Bleaching
Reductive bleaching is the most simple option for bleaching, not only because
just one chemical has to be added to the pulp, but also because the available low
or medium consistency after screening and latency chest can be applied. Other
than using an effective mixer and a tower or tube, no additional equipment is required.
Peroxide bleaching is more complicated, however. High-consistency dewatering
Is an essential requirement for bleaching effectiveness. Modern twin-wire presses
easily reach a consistency above 40%, and today – even when large amounts of
chemical must be added – consistency in the bleaching tower is well above 30%.
Four different chemicals must be mixed with the pulp. The chelant can be added
as a pre-treatment prior to the latency chest. Caustic soda, sodium silicate, and
hydrogen peroxide are either premixed with additional dilution water in a descending
cascade to a concentration of less than 10% H2O2 in the mixture. Alternatively,
these chemicals can be added directly, using a very effective mechanical
mixer, and mixed immediately with the pulp. Special attention must be paid to
the design of the chemical addition. A backflow of liquor into the storage tanks is
a serious safety threat, and may occur during a production halt. However, such a
hazard can be avoided by installing back-pressure valves, or even more effectively
by a system using the free flow of liquor into a small intermediate tank.
An example of a high-consistency peroxide bleach plant is shown in Fig. 6.12.
The retention time in the tower can be adjusted by controlling the filling height.
Mechanical discharge is essential for correct control, and older bleach plants operating
at a lower consistency (<25%) can be discharged by injecting water at the
base of the tower. An agitator (propeller) provides sufficient shear force to mix
water and fiber bundles to a uniform discharge consistency below 5%. At very
high consistency, simple stirring does not provide sufficient mixing, and the fiber
bundles and water remain separate. Discharge at a higher consistency requires
less volume of dilution water and allows post-bleaching with dithionite at medium
consistency after destruction of the peroxide excess with bisulfite. The second
twin-wire press is not required in the case of post-bleaching with dithionite. It is,
however, a technological advantage because it separates the water loop of the
bleach plant from the paper machine, and this may be important for retention
control. After an intense peroxide treatment the amount of anionic compounds
(“trash”) in the water circuit is high, and may cause problems.
Somewhat more complicated is a bleach plant with two peroxide stages
(Fig. 6.13). Three presses are required to allow recycling of the peroxide excess.
The pulp is dewatered to a high consistency, and excess liquor from the main
bleaching step is then added. This dilutes the consistency to a level between 10%
and 12%. In order to initiate a reaction, an addition of caustic soda to the peroxide
content might be required. Following this MC-stage, the next press generates the
high consistency required in the main bleaching stage. The effluent of this press